High Gloss High Speed

Some information

Lorem ipsum information

Corrosivity: C5 Very high corrosivity
Application: 2K Airless / 2K Airmix
Gloss: High gloss

Layer 1

306 DualCure Zinc Primer

Get quote

Product information

Aesthetic product properties:
Gloss: matt
Volume solids: ± 48 volume % (mixed product)
VOC: ≤ 485 gr/ltr.

Dry times (50μm):
Dust free: 20 minutes
Recoatable: 40 minutes (max. 7 days)

Test procedure:
Salt spray:
ISO 9227-NSS / ASTM B 117 >2.160 hours
Pull off (before/after test): ISO 4626 / ASTM D4541 7,0/5,0 MPa

Corrosion resistance:
TNO Electrochemical Impedance
Spectroscopy (EIS) R 2,7*109, n=0,95 (21 days)
Cathodic Disbonding ISO 15711 13 mm after 4200 hours

Flexibility:
ISO 1519 / ASTM D522 Cylindrical mandrel 19 mm
Pull off: ISO 4624 / ASTM D4541 7,0 MPa
Sa 2½ blasted steel

Processing

Airless spray
Thinner PU5801
Quantity 0-10 vol.%
Nozzle min 0,022 inch
Flow pressure min 150 bar
Dry film thickness 50-100 μm

Airmix Thinner PU5801
Quantity 0-10 vol.%
Nozzle min 0,022 inch
Flow pressure min 80 bar
Dry film thickness 50-100 μm

Cleaning tools: Immediately after application using thinner PU5801.

Packaging

Packaging:
10 litre cans. Thinner in 25 litre jerry cans and 200 litre drums.

Shelf life:
In original well shut packaging 12 months, stored inside at temperatures between 5°C and 40°C.

Layer 2

171i2 DualCure SX DTM Finish 60